Home>>Fabric

PVC Fabric
PVC fabric for inflatable boats 
 

 

Abrasion resistance:
The chemical formula of the outside PVC layer makes the material abrasive resistant and airtight properties: 200*170 N/5cm(± 20)

Chemical resistance:
Strong resistance to Hydrocarbon, Sunlight, Seawater, Oil and Fuel. Thanks to this properties which protect the material from fading and ageing.

Extreme condition resistance:
Low & High temperature resistance:
-30 + 70°C

Dimensional stability:
1% (24hrs-70°C)
Tensile and tear strength: 3800*3550 (± 250)

PVC Fabric Test Results:

Test Conducted

Result

Test Method

Warp

Weft

 

Tensile Strength 

 

533 lbs(240kg)

750lbs/5cm

(340kg/5cm)

 

533 lbs(240kg)

650lbs/5cm

(295kg/5cm)

 

FS-191A-5100(CRE) (GRAB TEST)

FS-191A-5100(CRE)

(CUT STRIP TEST)

 

Tear Strength

 40 lbs (18kg) 40 lbs (18kg)

FS-191A -5134(CRE)

(TRAPEZOID TEST)

FS -191A-5134(CRE)

(TONGUE TEST)
80 lbs (36kg) 100 lbs (45kg)

Adhesion Resistance (1inch)

25-35 lbs (11-16kg)

FS-191A-5970(CRE)
Resistance to low  Temperature No Cracking and Flecking  MIL - C - 20696 (-40C, -40F)
Colorfastness to Light 80 hours exposure 6-7 Grade AATCC 16E Xenon-arc-lamp
Resistance to Abrasion Weight Loss Face 1%, Back 1.3% Face 600 Cycle, Back 400 Cycle
 
TEST METHOD TEST ITEM UNIT RESULT
- - - APPILICATION - - - ARCHITECTURE
- - - ITEM - - - ADT NO.00017
- - - BASE FABRIC - - - 1100 Dtex,POLYESTER
- - - COATING MATERIAL - - -  PASTE
- - - FABRIC DENSITY Thread/Inch 28 / 26
DIN 53352 FINISHED WEIGHT gr/m2 1100   / 32OZ
DIN 53353 FINISHED THICKNESS m/m 0.9
DIN 53354 STRIP TENSILE Kgf/ 2Inch 340 / 300
  ELONGATION % 22 / 35
DIN 53363 TRAPIZOID TEAR Kgf 45 / 40
DIN 53357 ADHESION Kgf / Inch 7.8/ 6.8
DIN 53361 LOW TEMP.RESISTANCE degree C -25
- - - WARRANTY YEAR 3